Cellular Concrete Mix Design

Cellular light weight concrete clc is a light weight concrete that is produced by mixing cement and flyash slurry with pre formed foam.

Cellular concrete mix design.

Slowly start your mixing procedure by adding all sand then a little water and a little cement until all materials are in mixer making sure concrete is being mixed evenly. Our 4 equipment models are easy to operate reliable and predictable. It s useful for determining batch weights required amounts of water and concrete and calculating your costs. Advantages of clc blocks in construction.

Cellular concrete mix design both pervious impervious foamed concrete are available in densities starting at 20pcf wet cast which has a typical compressive strength at 28 days of 50psi up to 70pcf wet cast which has a typical compressive strength at 28 days of 1100psi. Get a quote get a quote. Canadian cellular concrete services inc. Contact us to discuss your project.

These clc blocks are competitive with red clay bricks in pricing and offer significant savings for finished structures. The typical density range is 20 60 lbs. Made in the usa. This causes the base mix to dramatically increase volume and reduce density.

Which develops a corresponding compressive strength range of 50 psi 930 psi. Has the knowledge and data available to help with preliminary design project budgets mix designs and placement parameters. Foam concrete also known as lightweight cellular concrete lcc low density cellular concrete ldcc discrete foamed concrete foam create cellular lightweight concrete or reduced density concrete is defined as a cement based slurry with a minimum of 20 per volume foam entrained into the plastic mortar. For over a decade cellular concrete technologies has provided mix designs to meet installation requirements for strength weight and r value with portable units for on the job projects to ready mix mounted units for large productions.

Foam concentrates must meet the standard astm c869 and c796 for use in cellular concrete. Canada cellular concrete contractor services the port mann. After materials are mixed well then add stable air. The water cement ratio can typically vary from 40 80 and the foam content is commonly as high as 80 depending on desired density.

Turn off mixer scrape off the sides of the drum then continue mixing. Geofill ld and geofill ld pervious mix designs are designed to create a product with a low density and resultant relatively lower compressive strength when compared to plain concrete. It will help you save time and hassle when creating mix designs and doing cost scenario analysis. A very basic cellular concrete mix design would consist simply of portland cement water and externally generated foam which is also referred to sometimes as preformed foam.